PBT/PC V3900WX 耐候性 沙伯基础PBT/PC V3900WX 抗紫外线 PBT/PC混合塑料
Tensile Stress, yld, Type I, 50 mm/min | 53 | MPa | ASTM D 638 | ||
---|---|---|---|---|---|
Tensile Stress, brk, Type I, 50 mm/min | 43 | MPa | ASTM D 638 | ||
Tensile Strain, yld, Type I, 50 mm/min | 5 | ASTM D 638 | |||
Tensile Strain, brk, Type I, 50 mm/min | 50 | ASTM D 638 | |||
Tensile Modulus, 5 mm/min | 2200 | MPa | ASTM D 638 | ||
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 80 | MPa | ASTM D 790 | ||
Flexural Modulus, 1.3 mm/min, 50 mm span | 2200 | MPa | ASTM D 790 | ||
Tensile Stress, yield, 50 mm/min | 51 | MPa | ISO 527 | ||
Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 | ||
Tensile Strain, yield, 50 mm/min | 4 | ISO 527 | |||
Tensile Strain, break, 50 mm/min | >40 | ISO 527 | |||
Tensile Modulus, 1 mm/min | 2090 | MPa | ISO 527 | ||
Flexural Stress, yield, 2 mm/min | 73 | MPa | ISO 178 | ||
Flexural Modulus, 2 mm/min | 2130 | MPa | ISO 178 | ||
IMPACT | |||||
Izod Impact, notched, 23°C | 800 | J/m | ASTM D 256 | ||
Izod Impact, notched, -30°C | 110 | J/m | ASTM D 256 | ||
Instrumented Impact Total Energy, 23°C | 50 | J | ASTM D 3763 | ||
Izod Impact, notched 80104 +23°C | 50 | kJ/m² | ISO 180/1A | ||
Izod Impact, notched 80104 0°C | 15 | kJ/m² | ISO 180/1A | ||
Izod Impact, notched 80104 -30°C | 10 | kJ/m² | ISO 180/1A | ||
Charpy 23°C, V-notch Edgew 80104 sp=62mm | 52 | kJ/m² | ISO 179/1eA | ||
THERMAL | |||||
Vicat Softening Temp, Rate B/50 | 105 | °C | ASTM D 1525 | ||
HDT, 1.82 MPa, 3.2mm, unannealed | 75 | °C | ASTM D 648 | ||
CTE, -40°C to 40°C, flow | 8.84E-05 | 1/°C | ASTM E 831 | ||
CTE, -40°C to 40°C, xflow | 8.97E-05 | 1/°C | ASTM E 831 | ||
CTE, -40°C to 40°C, flow | 8.84E-05 | 1/°C | ISO 11359-2 | ||
CTE, -40°C to 40°C, xflow | 8.97E-05 | 1/°C | ISO 11359-2 | ||
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | ||
Vicat Softening Temp, Rate B/50 | 121 | °C | ISO 306 | ||
Vicat Softening Temp, Rate B/120 | 123 | °C | ISO 306 | ||
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm | 77 | °C | ISO 75/Af | ||
Relative Temp Index, Elec | 120 | °C | UL 746B | ||
Relative Temp Index, Mech w/impact | 120 | °C | UL 746B | ||
Relative Temp Index, Mech w/o impact | 120 | °C | UL 746B | ||
PHYSICAL | |||||
Specific Gravity | 1.3 | - | ASTM D 792 | ||
Mold Shrinkage, flow, 3.2 mm (5) | 0.7-1 | SABIC method | |||
Melt Flow Rate, 266°C/5.0 kgf | 35 | g/10 min | ASTM D 1238 | ||
Density | 1.3 | g/cm³ | ISO 1183 | ||
Water Absorption, (23°C/sat) | 0.1 | ISO 62 | |||
Moisture Absorption (23°C / 50 RH) | 0.03 | ISO 62 | |||
Melt Volume Rate, MVR at 265°C/2.16 kg | 11 | cm³/10 min | ISO 1133 | ||
Melt Viscosity, 260°C, 1500 sec-1 | 260 | Pa-s | ISO 11443 | ||
FLAME CHARACTERISTICS | |||||
UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by SABIC-IP | ||
UL Compliant, 94-5VA Rating (3)(4) | 3 | mm | UL 94 by SABIC-IP | ||
UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 | ||
UL Recognized, 94-5VA Rating (3) | 3 | mm | UL 94 | ||
Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 | ||
Glow Wire Flammability Index 960°C, passes at, by VDE | 3 | mm | IEC 60695-2-12 | ||
Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 | ||
Glow Wire Ignitability Temperature, 3.0 mm | 725 | °C | IEC 60695-2-13 | ||
UV-light, water exposure/immersion | F1 | - | UL 746C |
PBT中文名称聚对苯二 丁酯,简称饱和聚酯,系高结晶性热可塑性塑料。
优点:1、机械性质安定抗张强度与抗张模数和尼龙相似;2、摩擦系数小有自润性;
3、吸水率低;4、电气性质优良;5、尺寸安定性良好;6、耐药品性、耐油性 。
用途:1、电子电器:无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等;
2、汽车:车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等;
3、工业零件:OA风扇、键盘、钓具卷线器、零件、灯罩等。