1100-630S台湾长春PBT塑胶原料增韧汽车连接器用，适合高拉拨力要求。原厂原包，提供原厂质量检验证书(COA)，1100-630S物性表等资料。
PBT 1100-630S物性表：
| Physical | Nominal Value | Unit | Test Method |
Density | 1.31 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 1.6 to 1.8 | % | |
Flow | 1.8 to 2.0 | % | |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 2200 | MPa | ISO 527-1 |
Tensile Stress (Break, 23°C) | 55.0 | MPa | ISO 527-2 |
Tensile Strain (Break, 23°C) | 60 | % | ISO 527-2 |
Flexural Modulus (23°C) | 2200 | MPa | ISO 178 |
Flexural Stress (23°C) | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (0.45 MPa, Unannealed) | 155 | °C | ISO 75-2/B |
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
Electric Strength (2.00 mm) | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating | HB | UL 94 |
| Processing Information | |||
| Injection | Nominal Value | Unit | |
Drying Temperature | 120 to 140 | °C | |
Drying Time | 4.0 | hr | |
Processing (Melt) Temp | 240 to 270 | °C | |
Mold Temperature | 60 to 100 | °C | |
为您精选
现货 PBT增强阻燃塑料 电子骨架继电器外壳
PBT台湾新光 E202G30 2886玻纤
PBT塑胶原料台湾长春4130-200K玻纤
阻燃级 德国巴斯夫PBT-B 4300 G3
日本宝理PBT 2002K ED3002 P
德国巴斯夫 Ultradur S4090G6
德国巴斯夫PBT Ultradur B430
增强级材料PBT日本宝理2002EF2001
高韧性PBT/台湾长春/1100非增强
德国巴斯夫PBTB4520非增强良好的流动性
发送询价单
您对该公司的咨询信息已成功提交，请注意接听供应商电话。
联系人信息
请输入您的称呼
请输入正确的联系方式
请选择咨询问题
请输入正确的图形验证码
提交成功
商家已收到您的消息，请注意接听供应商的来电～
确保商家能在第一时间与您取得联系
请留下您的联系方式
请输入正确的联系电话
请输入称呼或公司名称
换一张
请输入验证码