VALOX PBT/PET 815 加15%玻纤 光洁度好 沙伯基础PBT/PET 815
| Tensile Stress, yld, Type I, 5 mm/min | 100 | MPa | ASTM D 638 | ||
|---|---|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 100 | MPa | ASTM D 638 | ||
| Tensile Strain, yld, Type I, 50 mm/min | 3 | ASTM D 638 | |||
| Tensile Strain, brk, Type I, 50 mm/min | 3 | ASTM D 638 | |||
| Tensile Modulus, 5 mm/min | 6200 | MPa | ASTM D 638 | ||
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 155 | MPa | ASTM D 790 | ||
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 155 | MPa | ASTM D 790 | ||
| Flexural Modulus, 1.3 mm/min, 50 mm span | 5000 | MPa | ASTM D 790 | ||
| Hardness, Rockwell R | 120 | - | ASTM D 785 | ||
| Taber Abrasion, CS-17, 1 kg | 17 | mg/1000cy | SABIC method | ||
| Tensile Stress, yield, 5 mm/min | 100 | MPa | ISO 527 | ||
| Tensile Stress, break, 5 mm/min | 100 | MPa | ISO 527 | ||
| Tensile Strain, yield, 5 mm/min | 3 | ISO 527 | |||
| Tensile Strain, break, 5 mm/min | 3 | ISO 527 | |||
| Tensile Modulus, 1 mm/min | 6200 | MPa | ISO 527 | ||
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 | ||
| Flexural Stress, break, 2 mm/min | 145 | MPa | ISO 178 | ||
| Flexural Strain, break, 2 mm/min | 4 | ISO 178 | |||
| Flexural Modulus, 2 mm/min | 5200 | MPa | ISO 178 | ||
| Hardness, H358/30 | 102 | MPa | ISO 2039-1 | ||
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | ||
| IMPACT | |||||
| Charpy Impact, unnotched, 23°C | 30 | kJ/m² | ISO 179/2C | ||
| Charpy Impact, unnotched, -30°C | 30 | kJ/m² | ISO 179/2C | ||
| Izod Impact, unnotched, 23°C | 390 | J/m | ASTM D 4812 | ||
| Izod Impact, unnotched, -30°C | 390 | J/m | ASTM D 4812 | ||
| Izod Impact, notched, 23°C | 60 | J/m | ASTM D 256 | ||
| Izod Impact, notched, 0°C | 60 | J/m | ASTM D 256 | ||
| Izod Impact, notched, -30°C | 60 | J/m | ASTM D 256 | ||
| Izod Impact, unnotched 80104 +23°C | 30 | kJ/m² | ISO 180/1U | ||
| Izod Impact, unnotched 80104 -30°C | 25 | kJ/m² | ISO 180/1U | ||
| Izod Impact, notched 80104 +23°C | 6 | kJ/m² | ISO 180/1A | ||
| Izod Impact, notched 80104 0°C | 6 | kJ/m² | ISO 180/1A | ||
| Izod Impact, notched 80104 -30°C | 6 | kJ/m² | ISO 180/1A | ||
| Charpy 23°C, V-notch Edgew 80104 sp=62mm | 5 | kJ/m² | ISO 179/1eA | ||
| Charpy Impact, notched, 23°C | 7 | kJ/m² | ISO 179/2C | ||
| Charpy -30°C, V-notch Edgew 80104 sp=62mm | 4 | kJ/m² | ISO 179/1eA | ||
| Charpy Impact, notched, -20°C | 7 | kJ/m² | ISO 179/2C | ||
| Charpy 23°C, Unnotch Edgew 80104 sp=62mm | 30 | kJ/m² | ISO 179/1eU | ||
| Charpy -30°C, Unnotch Edgew 80104 sp=62mm | 30 | kJ/m² | ISO 179/1eU | ||
| THERMAL | |||||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ASTM D 1525 | ||
| Vicat Softening Temp, Rate B/50 | 204 | °C | ASTM D 1525 | ||
| HDT, 0.45 MPa, 6.4 mm, unannealed | 210 | °C | ASTM D 648 | ||
| HDT, 1.82 MPa, 6.4 mm, unannealed | 160 | °C | ASTM D 648 | ||
| CTE, -40°C to 40°C, flow | 4.5E-05 | 1/°C | ASTM E 831 | ||
| CTE, -40°C to 40°C, xflow | 9.32E-05 | 1/°C | ASTM E 831 | ||
| CTE, 60°C to 138°C, flow | 5.4E-05 | 1/°C | ASTM E 831 | ||
| Thermal Conductivity | 0.19 | W/m-°C | ISO 8302 | ||
| CTE, -40°C to 40°C, flow | 3.23E-05 | 1/°C | ISO 11359-2 | ||
| CTE, -40°C to 40°C, xflow | 7.2E-05 | 1/°C | ISO 11359-2 | ||
| CTE, 23°C to 80°C, flow | 5.5E-05 | 1/°C | ISO 11359-2 | ||
| CTE, 23°C to 80°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 | ||
| CTE, 23°C to 150°C, flow | 2.41E-05 | 1/°C | ISO 11359-2 | ||
| CTE, 23°C to 150°C, xflow | 1.76E-04 | 1/°C | ISO 11359-2 | ||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | ||
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 | ||
| Vicat Softening Temp, Rate B/50 | 204 | °C | ISO 306 | ||
| Vicat Softening Temp, Rate B/120 | 200 | °C | ISO 306 | ||
| HDT/Be, 0.45MPa Edgew 120104 sp=100mm | 210 | °C | ISO 75/Be | ||
| HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm | 175 | °C | ISO 75/Ae | ||
| HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm | 210 | °C | ISO 75/Bf | ||
| HDT/Af, 1.8 MPa Flatw 80104 sp=64mm | 167 | °C | ISO 75/Af | ||
| Relative Temp Index, Elec | 125 | °C | UL 746B | ||
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B | ||
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B | ||
| PHYSICAL | |||||
| Specific Gravity | 1.43 | - | ASTM D 792 | ||
| Specific Volume | 0.7 | cm³/g | ASTM D 792 | ||
| Water Absorption, 24 hours | 0.06 | ASTM D 570 | |||
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.4-0.8 | SABIC method | |||
| Mold Shrinkage, flow, 1.5-3.2 mm (5) | 0.4-0.6 | SABIC method | |||
| Mold Shrinkage, flow, 3.2-4.6 mm (5) | 0.6-0.9 | SABIC method | |||
| Mold Shrinkage on Tensile Bar, xflow (2) (5) | 0.6-1 | SABIC method | |||
| Mold Shrinkage, xflow, 1.5-3.2 mm (5) | 0.5-0.8 | SABIC method | |||
| Mold Shrinkage, xflow, 3.2-4.6 mm (5) | 0.8-1.1 | SABIC method | |||
| Melt Flow Rate, 250°C/5.0 kgf | 20 | g/10 min | ASTM D 1238 | ||
| Melt Flow Rate, 265°C/5.0 kgf | 60 | g/10 min | ASTM D 1238 | ||
| Density | 1.43 | g/cm³ | ISO 1183 | ||
| Water Absorption, (23°C/sat) | 0.26 | ISO 62 | |||
| Moisture Absorption (23°C / 50 RH) | 0.06 | ISO 62 | |||
| Melt Volume Rate, MVR at 265°C/1.2 kg | 12 | cm³/10 min | ISO 1133 | ||
| Melt Volume Rate, MVR at 265°C/5.0 kg | 50 | cm³/10 min | ISO 1133 | ||
| Melt Viscosity, 260°C, 1500 sec-1 | 155 | Pa-s | ISO 11443 | ||
| ELECTRICAL | |||||
| Volume Resistivity | 56000000000 | Ohm-cm | ASTM D 257 | ||
| Dielectric Strength, in air, 3.2 mm | 22 | kV/mm | ASTM D 149 | ||
| Dielectric Strength, in oil, 1.6 mm | 23.6 | kV/mm | ASTM D 149 | ||
| Relative Permittivity, 100 Hz | 3.6 | - | ASTM D 150 | ||
| Relative Permittivity, 1 MHz | 3.5 | - | ASTM D 150 | ||
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 | ||
| Arc Resistance, Tungsten PLC | 5 | PLC Code | ASTM D 495 | ||
| Hot Wire Ignition PLC) | 2 | PLC Code | UL 746A | ||
| High Voltage Arc Track Rate PLC | 1 | PLC Code | UL 746A | ||
| High Ampere Arc Ign, surface PLC | 2 | PLC Code | UL 746A | ||
| Comparative Tracking Index (UL) PLC | 2 | PLC Code | UL 746A | ||
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | ||
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | ||
| Dielectric Strength, shorttime, 1.0mm | 18 | kV/mm | IEC 60243-1 | ||
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 | ||
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 | ||
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 | ||
| Relative Permittivity, 100 Hz | 3.6 | - | IEC 60250 | ||
| Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 | ||
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 | ||
| Dissipation Factor, 100 Hz | 0.002 | - | IEC 60250 | ||
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 | ||
| Comparative Tracking Index | 325 | V | IEC 60112 | ||
| Comparative Tracking Index, M | 175 | V | IEC 60112 | ||
| Relative Permittivity, 50/60 Hz | 3 | - | IEC 60250 | ||
| FLAME CHARACTERISTICS | |||||
| UL Recognized, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 | ||
| UL Recognized, 94HB Flame Class Rating 2nd value (3) | 3 | mm | UL 94 | ||
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 |
PBT简称饱和聚酯，系高结晶性热可塑性塑料。
优点：1、机械性质安定抗张强度与抗张模数和尼龙相似；2、摩擦系数小有自润性；
3、吸水率低；4、电气性质优良；5、尺寸安定性良好；6、耐药品性、耐油性。
用途：1、电子电器：无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等；
2、汽车：车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等；
3、工业零件：OA风扇、键盘、钓具卷线器、零件、灯罩等。
为您精选
阻燃级 德国巴斯夫PBT-B 4300 G3
PBT台湾新光 E202G30 2886玻纤
PBT塑胶原料台湾长春4130-200K玻纤
日本宝理PBT 2002K ED3002 P
553-7001 30纤 阻燃PBT VAL
357U BK1066 抗UV 耐候 阻燃P
德国巴斯夫PBT Ultradur B430
310SEO-7001黑色 未增强 阻燃PB
310SEO-1001本色 未增强 阻燃PB
364-BK1066 阻燃V0的PBT VA
发送询价单
您对该公司的咨询信息已成功提交，请注意接听供应商电话。
联系人信息
请输入您的称呼
请输入正确的联系方式
请选择咨询问题
请输入正确的图形验证码
提交成功
商家已收到您的消息，请注意接听供应商的来电～
确保商家能在第一时间与您取得联系
请留下您的联系方式
请输入正确的联系电话
请输入称呼或公司名称
换一张
请输入验证码