Density密度 

1.27 g/cc

0.0459 lb/in³

ISO 1183

1.08 g/cc
@Temperature 300 °C

0.0390 lb/in³
@Temperature 572 °F

Melt

Water Absorption吸水率 

0.26 %

0.26 %

Similar to ISO 62

Moisture Absorption at Equilibrium吸湿平衡 

0.10 %

0.10 %

Similar to ISO 62

Linear Mold Shrinkage, Flow线性收缩率/流动 

0.0060 cm/cm

0.0060 in/in

parallel; ISO 294-4,2577

Linear Mold Shrinkage, Transverse线性收缩率/横向 

0.0050 cm/cm

0.0050 in/in

ISO 294-4,2577

Melt Flow熔体流动速率 

6.5 g/10 min
@Load 1.20 kg,
Temperature 300 °C

6.5 g/10 min
@Load 2.65 lb,
Temperature 572 °F

ISO 1133

Mechanical Properties力学性能

Metric公制数据

English英制数据

Comments测试方法

Tensile Strength at Break 

45.0 MPa

6530 psi

ISO 527-1/-2

Elongation at Break断裂伸长率 

15 %

15 %

ISO 527-1/-2

Tensile Modulus拉伸模量 

3.80 GPa

551 ksi

ISO 527-1/-2

Impact冲击

4000

4000

Puncture - maximum force (N); ISO 6603-2

3700
@Temperature -30.0 °C

3700
@Temperature -22.0 °F

Puncture - maximum force (N); ISO 6603-2

Puncture Energy穿刺强度 

25.0 J

18.4 ft-lb

ISO 6603-2

15.0 J
@Temperature -30.0 °C

11.1 ft-lb
@Temperature -22.0 °F

ISO 6603-2

Tensile Creep Modulus, 1 hour拉伸蠕变模量，1小时 

3600 MPa

522000 psi

ISO 899-1

Tensile Creep Modulus, 1000 hours拉伸蠕变模量，1000小时 

2900 MPa

421000 psi

ISO 899-1

Electrical Properties电性能

Metric公制数据

English英制数据

Comments测试方法

Volume ResiSTivity体积电阻率 

>= 1.00e+13 ohm-cm

>= 1.00e+13 ohm-cm

IEC 60093

Surface Resistance表面电阻 

>= 1.00e+15 ohm

>= 1.00e+15 ohm

IEC 60093

Dielectric Constant介电常数 

3.2
@Frequency 100 Hz

3.2
@Frequency 100 Hz

IEC 60250

3.2
@Frequency 1.00e+6 Hz

3.2
@Frequency 1.00e+6 Hz

IEC 60250

Dielectric Strength介电强度 

36.0 kV/mm

914 kV/in

IEC 60243-1

Dissipation Factor耗散因数 

0.0010
@Frequency 100 Hz

0.0010
@Frequency 100 Hz

IEC 60250

0.0090
@Frequency 1.00e+6 Hz

0.0090
@Frequency 1.00e+6 Hz

IEC 60250

Comparative Tracking Index漏电起痕指数 

175 V

175 V

IEC 6011