牌号 : |
2200RGC9AT |
加工级别 : |
注塑级 |
特性级别 : |
阻燃级,高流动 |
用途级别 : |
通用级 |
品牌 : |
沙伯基础 |
产地 : |
广州南沙 |
品名 : |
PC |
是否进口 : |
否 |
厂家(产地) : |
沙伯基础(南沙) |
货号 : |
55255 |
产品详情
Product details
PC2200树脂是一个高流量(生产商= 22 300 ? C / 1.2公斤),热稳定,聚碳酸酯产品设计用于自定义复合市场。它不包含紫外线稳定剂或脱模。
| Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min | 640 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | >70 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 23900 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 910 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 23400 | kgf/cm2 | ASTM D 790 | |
| Hardness, Rockwell R | 120 | - | ASTM D 785 | |
| Tensile Stress, yield, 50 mm/min | 63 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | >70 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2350 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 | |
| Hardness, Rockwell R | 120 | - | ISO 2039-2 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | NB | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 65 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Energy @ peak, 23°C | 560 | cm-kgf | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | NB | kJ/m2 | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | NB | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 65 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 12 | kJ/m2 | ISO 180/1A | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 140 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm | 133 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2 mm | 122 | °C | ASTM D 648 | |
| CTE, -40°C to 95°C, flow | 7.E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity | 0.2 | W/m-°C | ASTM C 177 | |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 | |
| CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 140 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 133 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.2 | - | ASTM D 792 | |
| Water Absorption, equilibrium, 23C | 0.35 | % | ASTM D 570 | |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.5 - 0.7 | % | SABIC Method | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method | |
| Melt Flow Rate, 300°C/1.2 kgf | 22 | g/10 min | ASTM D 1238 | |
| Density | 1.2 | g/cm3 | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 21 | cm3/10 min | ISO 1133 | |
| OPTICAL | Value | Unit | Standard | |
| Light Transmission, 2.54 mm | 88 - 90 | % | ASTM D 1003 | |
| Haze, 2.54 mm | <0.8 | % | ASTM D 1003 | |
| Refractive Index | 1.586 | - | ASTM D 542 | |
| Refractive Index | 1.586 | - | ISO 489 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 | |
| Dielectric Strength, 1.6 mm | 27 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 60 Hz | 3 | - | ASTM D 150 | |
| Relative Permittivity, 1 MHz | 3 | - | ASTM D 150 | |
| Dissipation Factor, 60 Hz | 0.001 | - | ASTM D 150 | |
| Dissipation Factor, 1 MHz | 0.01 | - | ASTM D 150 | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Dielectric Strength, 1.6 mm | 27 | kV/mm | IEC 60243-1 | |
| Relative Permittivity, 60 Hz | 3 | - | IEC 60250 | |
| Relative Permittivity, 1 MHz | 3 | - | IEC 60250 | |
| Dissipation Factor, 60 Hz | 0.001 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94V-2 Flame Class Rating (3) | 1.5 | mm | UL 94 | |
| Source GMD, last updated:2012/07/10 |
| Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 280 - 300 | °C |
| Nozzle Temperature | 270 - 290 | °C |
| Front - Zone 3 Temperature | 280 - 300 | °C |
| Middle - Zone 2 Temperature | 270 - 290 | °C |
| Rear - Zone 1 Temperature | 260 - 280 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 80 - 100 | °C |
温馨提示您:
因本页面展示有限无法完全描述产品更多相关信息；塑胶原料行情每天每时波动较大无法及时更新，请亲们理解！
产品信息和最新价格请您及时来电！
搜好货供应商东莞市胜浩塑胶原料有限公司供应PC 2200RGC9AT 沙伯基础 高流动PC 阻燃注塑级PC，为您提供详细的产品报价、参数、图片等商品信息，如需进一步了解PC 2200RGC9AT 沙伯基础 高流动PC 阻燃注塑级PC，请与厂家直接联系，请在联系时说明是在搜好货网看到这条商机的。
为您精选
-
耐寒PVC 可以达到零下45℃ 不易挥发分解
¥26.50 -
PVC增塑剂 增韧PVC氯化聚乙烯抗寒剂 零
¥26.50 -
非牵移ABS改性剂 氯化橡胶 透明液体橡胶
¥26.50 -
可发泡液体橡胶LGCR工业发泡制品用液体氯化
¥26.50 -
PVC皮革或软管材 PVC线材等制品耐折PV
¥26.50
-
超耐低温橡胶零下45℃无脆化PVC抗寒性好用
¥26.50 -
长效抗静电剂 PE薄膜防静电母粒 聚乙烯
¥118 -
长久PE抗静电剂 PE长久防静电母粒 制品表
¥118 -
3000目 PTFE粉 聚四氟乙烯微粉 胜浩
¥120 -
欧盟环保级PTFE细粉 3000目 4微米
¥120