Lexan* EXRL0763 is a co-polycarbonate resin with improved scratch and abrasion resistance compared to standard polycarbonate. Lexan* EXRL0763 is available in transparent colors
TYPICAL PROPERTIES (1) | ||||
MECHANICAL机械性能 | Value | Unit | Standard | |
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min | 80 | MPa | ISO 527 | |
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min | 60 | MPa | ISO 527 | |
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min | 7 | % | ISO 527 | |
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min | 38 | % | ISO 527 | |
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min | 2660 | MPa | ISO 527 | |
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min | 113 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min | 2630 | MPa | ISO 178 | |
IMPACT | Value | Unit | Standard | |
Izod IMPACT, unnotched 80*10*3 +23°C | NB | kJ/m² | ISO 180/1U | |
Izod IMPACT, unnotched 80*10*3 -30°C | 69 | kJ/m² | ISO 180/1U | |
Izod IMPACT, notched 80*10*3 +23°C / 悬壁梁缺口冲击强度, 80*10*3 +23°C | 8 | kJ/m² | ISO 180/1A | |
Izod IMPACT, notched 80*10*3 -30°C / 悬壁梁缺口冲击强度, 80*10*3 -30°C | 6 | kJ/m² | ISO 180/1A | |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*3 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度,-30°C,C80*10*3 sp=62mm | 4 | kJ/m² | ISO 179/1eA | |
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | NB | kJ/m² | ISO 179/1eU | |
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 52 | kJ/m² | ISO 179/1eU | |
THERMAL | Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50 | 126 | °C | ISO 306 | |
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120 | 128 | °C | ISO 306 | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距 | 107 | °C | ISO 75/Af | |
PHYSICAL | Value | Unit | Standard | |
Density/密度 | 1.17 | g/cm³ | ISO 1183 | |
Melt Volume Rate, MVR at 300°C/1.2 kg | 18 | cm³/10 min | ISO 1133 | |
OPTICAL | Value | Unit | Standard | |
Light Transmission/透光率, 2.54 mm | 88 | % | ASTM D 1003 | |
Haze/雾度, 2.54 mm | <0.8 | % | ASTM D 1003 | |
Refractive Index /折射指数 | 1.584 | - | ASTM D 542 | |
Refractive Index /折射指数 | 1.584 | - | ISO 489 |
Source GMD, last updated:2009/12/29 |
Processing |
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature / 干燥温度 | 110 | °C |
Drying Time / 干燥时间 | 3 - 4 | hrs |
Maximum Moisture Content / 超大含湿量 | 0.02 | % |
Melt Temperature / 熔体温度 | 260 - 280 | °C |
Nozzle Temperature / 注嘴温度 | 250 - 270 | °C |
Front - Zone 3 Temperature / 前区3温度 | 260 - 280 | °C |
Middle - Zone 2 Temperature / 中区2温度 | 250 - 270 | °C |
Rear - Zone 1 Temperature / 后区1温度 | 240 - 260 | °C |
Hopper Temperature / 料筒温度 | 40 - 60 | °C |
Mold Temperature / 模具温度 | 60 - 85 | °C |
S ource GMD, last updated:2009/12/29 |
温馨提示您:
因本页面展示有限无法完全描述产品更多相关信息;塑胶原料行情每天每时波动较大无法及时更新,个别货物可能存在新旧包装,请亲们理解!产品信息和近期价格请您及时来电!
搜好货供应商东莞市胜浩塑胶原料有限公司供应共聚PC Lexan EXRL0763-NA9E104T 耐刮伤PC 耐磨PC 沙伯基础,为您提供详细的产品报价、参数、图片等商品信息,如需进一步了解共聚PC Lexan EXRL0763-NA9E104T 耐刮伤PC 耐磨PC 沙伯基础,请与厂家直接联系,请在联系时说明是在搜好货网看到这条商机的。
联系方式
Contact information
真诚期待您的来电
- 东莞市胜浩塑胶原料有限公司
- 叶庚胜 销售部
- 13620043019
- 广东省东莞市樟木头镇塑胶商务中心7栋56号
为您精选
PC相关商机
- PC EX9330L 无卤阻燃 低介电常数EX9330L户外通讯设备外壳材料
- 抗老化不发黄 超韧耐寒PC 耐老化耐候性 户外产品专用材料
- 可通过双85老化测试超韧耐寒PC 耐老化耐候性 新能源充电桩外壳专用材料
- PC EX9330L 超韧耐寒PC 低介电常数EX9330L户外通讯设备外壳材料
- 抗紫外线/耐水解/抗老化耐候性/无卤阻燃/PC EX9330L/充电桩转换接头专用料
- 5G电子设备外壳专用原料/阻燃PC EX9330L/无卤阻燃透波性EX9330L
- Iupilon日本三菱EHR3100 遮光阻燃PC EHR3100 光反射材料
- 无卤防火耐候性PC/沙伯基础EXL9330/耐水解抗紫外线EXL9330
- 5G天线外壳指定原料/无卤阻燃PC EX9330L/低介电透波性EX9330L
- 耐候性/无卤阻燃/PC EX9330L/低介电透波性EX9330L/5G雷达天线外壳专用材料
- 超韧耐寒PC EXL9330 可通过双85湿热老化测试
- PC EX9330L 耐雨水酸碱 低介电常数EX9330L户外通讯设备外壳材料
猜你在找
推荐厂家
查看更多
此共聚PC Lexan EXRL0763-NA9E104T 耐刮伤PC 耐磨PC 沙伯基础产品由东莞市胜浩塑胶原料有限公司在2019-05-21T03:23:42更新,主要更新内容为:产品详情,产品促销语,产品起订价,产品起订量,产品类别信息。