产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 比重 | ASTM D792, ISO 1183 | 1.39 | g/cm3; | |
| 熔体质量流动速率 | 190/2.16kg | ASTM D1238 | 27 | g/10 min | |
| 熔体质量流动速率 | ISO 1133 | 27 | g/10 min | ||
| 成型收缩率 | flow,3.00MM | ASTM D955 | 2.0 | ||
| 成型收缩率 | 3.00mm | ISO 294-4 | 2.0 | ||
| 吸水率 | Equilibrium,23,60rh | ASTM D570 | 0.22 | ||
| 洛氏硬度 | M-Scale | ASTM D785 | 80 | ||
| 机械性能 | 拉伸强度 | Yield,23 | |||
| ASTM D638 | 55.0 | MPa | |||
| 拉伸强度 | Yield,23 | ||||
| ISO 527-2 | 57.0 | MPa | |||
| 拉伸伸长率 | Break,23 | ||||
| ASTM D638 | 55 | ||||
| 拉伸伸长率 | Break,23 | ||||
| ISO 527-2 | 35 | ||||
| 弯曲模量 | 23°C | ASTM D790, ISO 178 | 2500 | MPa | |
| 弯曲强度 | 23°C | ASTM D790 | 80.0 | MPa | |
| 弯曲强度 | 23°C | ISO 178 | 83.0 | MPa | |
| 摩擦系数 | Vs.Itself-Dynamic | ASTM D1894 | 0.16 | ||
| 摩擦系数 | Vs.Metal-Dynamic | ASTM D1894 | 0.21 | ||
| Charpy无缺口冲击强度 | ISO 179/1eA | 6.0 | kJ/m2; | ||
| Izod缺口冲击强度 | 3.20mm | ASTM D256 | 69.0 | J/m | |
| 电气性能 | 表面电阻率 | ASTM D257 | 1.0E+16 | ohms | |
| 体积电阻率 | ASTM D257 | 1.0E+14 | ohm·cm | ||
| 表面电阻率 | IEC 60093 | 1.0E+14 | ohms | ||
| 体积电阻率 | IEC 60093 | 1.0E+12 | ohm·cm | ||
| 电气强度 | IEC 60243-1 | 19 | kV/mm | ||
| 热性能 | 热畸变温度 | 0.45MPa,未退火 | ASTM D648 | 158 | °C |
| 热畸变温度 | 1.8MPa,未退火 | ASTM D648 | 110 | °C | |
| 热畸变温度 | 1.8MPa,未退火 | ISO 75-2/A | 95.0 | °C | |
| 熔融温度 | ASTM D3418 | 165 | °C | ||
| 线性热膨胀系数 | flow,20 to 80°C | ASTM D696 | 0.00013 | cm/cm/°C | |
| 其它性能 | 阻燃等级 | 0.8mm | UL 94 | HB | |
为您精选
POM日本宝理 M90-44 高刚性pom
转动机械零件专用材料 韩国可隆POM K90
韩国可隆POM K900 各种齿轮专用材料
韩国可隆POM K900 电子开关零件指定材
韩国可隆POM K900 汽车内外部把手材料
高刚性美国杜邦聚甲醛POM900P包装容器
美国杜邦POM高压管塑料/100TL/POM
POM日本宝理 GH-20 pom M90-
防静电POM棒材料 ED-10韩国工程塑料
POM 日本宝理 SW-01 耐磨 高滑动
发送询价单
您对该公司的咨询信息已成功提交，请注意接听供应商电话。
联系人信息
请输入您的称呼
请输入正确的联系方式
请选择咨询问题
请输入正确的图形验证码
提交成功
商家已收到您的消息，请注意接听供应商的来电～
确保商家能在第一时间与您取得联系
请留下您的联系方式
请输入正确的联系电话
请输入称呼或公司名称
换一张
请输入验证码