PC/ABS MC8002 高冲击 沙伯基础 PC/ABS MC8002 高冲击合金塑料
Tensile Stress, yld, Type I, 50 mm/min | 56 | MPa | ASTM D 638 | ||
---|---|---|---|---|---|
Tensile Strain, yld, Type I, 50 mm/min | 5 | ASTM D 638 | |||
Tensile Strain, brk, Type I, 50 mm/min | 150 | ASTM D 638 | |||
Tensile Modulus, 50 mm/min | 2200 | MPa | ASTM D 638 | ||
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 86 | MPa | ASTM D 790 | ||
Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 | ||
IMPACT | |||||
Izod Impact, notched, 23°C | 640 | J/m | ASTM D 256 | ||
Izod Impact, notched, -30°C | 534 | J/m | ASTM D 256 | ||
Instrumented Impact Total Energy, 23°C | 61 | J | ASTM D 3763 | ||
Instrumented Impact Total Energy, -30°C | 54 | J | ASTM D 3763 | ||
THERMAL | |||||
HDT, 0.45 MPa, 3.2 mm, unannealed | 123 | °C | ASTM D 648 | ||
HDT, 1.82 MPa, 3.2mm, unannealed | 107 | °C | ASTM D 648 | ||
HDT, 1.82 MPa, 6.4 mm, unannealed | 110 | °C | ASTM D 648 | ||
CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ASTM E 831 | ||
Thermal Conductivity | 0.2 | W/m-°C | ASTM C177 | ||
PHYSICAL | |||||
Specific Gravity | 1.14 | - | ASTM D 792 | ||
Water Absorption, 24 hours | 0.1 | ASTM D 570 | |||
Water Absorption, equilibrium, 23C | 0.4 | ASTM D 570 | |||
Mold Shrinkage, flow, 3.2 mm (5) | 0.5-0.7 | SABIC method | |||
Melt Flow Rate, 260°C/5.0 kgf | 9 | g/10 min | ASTM D 1238 |
PC/ABS中文名称聚碳酸酯和 -丁二烯- 共聚物,系塑料合金。
优点:增加ABS耐热尺寸安定性、改善PC低温、后壁耐冲性、降低成本。
用途:计算机设备外壳、计算机其他组件、打字机外壳、照相机、手机及其它商业机器的壳体、电器设备、电子电器零件、小家电零组件、电吹风、接插件、文字处理器、医疗设备零组件、办公用品、化妆品容器、食物餐盘、草坪和园艺机器、汽车头灯框、尾灯外罩、仪表板、内部装修以及车轮盖等。