PC/ABS CS9610 阻燃级 沙伯基础 PC/ABS CS9610 阻燃电气设备合金塑料
Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D 638 | ||
---|---|---|---|---|---|
Tensile Stress, brk, Type I, 50 mm/min | 62 | MPa | ASTM D 638 | ||
Tensile Strain, yld, Type I, 50 mm/min | 5 | ASTM D 638 | |||
Tensile Strain, brk, Type I, 50 mm/min | 55 | ASTM D 638 | |||
Tensile Modulus, 50 mm/min | 2600 | MPa | ASTM D 638 | ||
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 98 | MPa | ASTM D 790 | ||
Flexural Modulus, 1.3 mm/min, 50 mm span | 2440 | MPa | ASTM D 790 | ||
Tensile Stress, yield, 50 mm/min | 62 | MPa | ISO 527 | ||
Tensile Stress, break, 50 mm/min | 50 | MPa | ISO 527 | ||
Tensile Strain, yield, 50 mm/min | 4.8 | ISO 527 | |||
Tensile Strain, break, 50 mm/min | >45 | ISO 527 | |||
Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 | ||
Flexural Stress, yield, 2 mm/min | 98 | MPa | ISO 178 | ||
Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 | ||
IMPACT | |||||
Izod Impact, notched, 23°C | 800 | J/m | ASTM D 256 | ||
Instrumented Impact Total Energy, 23°C | 72 | J | ASTM D 3763 | ||
Izod Impact, notched 80103 +23°C | 45 | kJ/m² | ISO 180/1A | ||
Izod Impact, notched 80103 -30°C | 15 | kJ/m² | ISO 180/1A | ||
Charpy 23°C, V-notch Edgew 80103 sp=62mm | 45 | kJ/m² | ISO 179/1eA | ||
Charpy -30°C, V-notch Edgew 80103 sp=62mm | 15 | kJ/m² | ISO 179/1eA | ||
THERMAL | |||||
HDT, 0.45 MPa, 3.2 mm, unannealed | 118 | °C | ASTM D 648 | ||
HDT, 1.82 MPa, 3.2mm, unannealed | 105 | °C | ASTM D 648 | ||
Vicat Softening Temp, Rate B/50 | 124 | °C | ISO 306 | ||
Vicat Softening Temp, Rate B/120 | 127 | °C | ISO 306 | ||
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm | 106 | °C | ISO 75/Af | ||
PHYSICAL | |||||
Specific Gravity | 1.2 | - | ASTM D 792 | ||
Mold Shrinkage, flow, 3.2 mm (5) | 0.4-0.6 | SABIC method | |||
Melt Flow Rate, 260°C/5.0 kgf | 15 | g/10 min | ASTM D 1238 | ||
Melt Volume Rate, MVR at 260°C/5.0 kg | 12 | cm³/10 min | ISO 1133 | ||
FLAME CHARACTERISTICS | |||||
UL Recognized, 94V-0 Flame Class Rating (3) | 2 | mm | UL 94 | ||
UL Recognized, 94-5VB Rating (3) | 2 | mm | UL 94 | ||
NBS Smoke Density, Flaming, Dmax | 225 | - | ASTM E 662 | ||
NBS Smoke Density, Flaming, Ds 1.5 min | 40 | - | ASTM E 662 | ||
NBS Smoke Density, Flaming, Ds 4 min | 150 | - | ASTM E 662 |
PC/ABS中文名称聚碳酸酯和 -丁二烯- 共聚物,系塑料合金。
优点:增加ABS耐热尺寸安定性、改善PC低温、后壁耐冲性、降低成本。
用途:计算机设备外壳、计算机其他组件、打字机外壳、照相机、手机及其它商业机器的壳体、电器设备、电子电器零件、小家电零组件、电吹风、接插件、文字处理器、医疗设备零组件、办公用品、化妆品容器、食物餐盘、草坪和园艺机器、汽车头灯框、尾灯外罩、仪表板、内部装修以及车轮盖等。